Effect of Chemical Pressure on High Temperature Ferrimagnetic Double Perovskites Sr2CrOsO6 and Ca2CrOsO6

Abstract: The ordered double perovskites Sr2CrOsO6 and Ca2CrOsO6 have been synthesized and characterized with neutron powder diffraction, electrical transport measurements, and high field magnetization experiments. Sr2CrOsO6 and Ca2CrOsO6 crystallize with R-3 and P21/n space group symmetry, respectively. Both materials are found to be ferrimagnetic insulators with saturation magnetizations near 0.2 {\mu}B. Sr2CrOsO6 orders at 660 K, showing non-monotonic magnetization temperature dependence, while Ca2CrOsO6 orders at 490 K and does not show non-monotonic behavior. Evidence for a theoretically predicted canted magnetic structure in Sr2CrOsO6 is sought and not found.