Saturation of ion irradiation effects in Cr2AlC

Abstract: Cr2AlC materials were irradiated with 7 MeV Xe26+ ions and 500 keV He2+ ions at room temperature. A structural transition with an increased c lattice parameter and a decreased a lattice parameter occurs after irradiation to doses above 1 dpa. Nevertheless, the modified structure is stable up to the dose of 5.2 dpa without obvious lattice disorder. The three samples irradiated to doses above 1 dpa have comparable lattice parameters and hardness values, suggesting a saturation of irradiation effects in Cr2AlC. The structural transition and irradiation effects saturation are ascribed to irradiation-induced antisite defects (CrAl and AlCr) and C interstitials, which is supported by the calculations of the formation energies of various defects in Cr2AlC. The irradiation-induced antisite defects and C interstitials may be critical to understand the excellent resistance to irradiation-induced amorphization of MAX phases.