Perpendicular magnetic anisotropy of an ultrathin Fe layer grown on NiO(001)

Abstract: The magnetic anisotropy and magnetic interactions at the interface between Fe and NiO(001) were investigated. Depending on the growth conditions of the NiO(001) layers and the post-annealing temperature, the preferential magnetization direction of the ultrathin Fe layer grown on a NiO(001) layer changed from in-plane to a direction perpendicular to the film plane. The lattice constant of the NiO(001) layers parallel to the growth direction increased with O$_2$ flow rate, while that parallel to the in-plane were locked onto the MgO(001) substrate regardless of the growth conditions of the NiO layers. Moreover, perpendicular magnetization was observed only when the NiO layer was grown with O$_2$ flow rates higher than 2.0 sccm corresponding to oxygen-rich NiO. X-ray magnetic circular dichroism measurements revealed an enhancement in anisotropic orbital magnetic moments similar to the origin of perpendicular magnetic anisotropy at the Fe/MgO(001) interface. The interfacial magnetic anisotropy energies were 0.93 and 1.02 mJ/m$^2$ at room temperature and at 100 K, respectively, indicating less temperature dependence. In contrast, the coercivity $H_c$ exhibited a significant temperature dependence. Although no signature of exchange bias or unidirectional loop shift was observed, $H_c$ was strongly dependent on the NiO layer thickness, indicating that the exchange interaction at the interface between the ferromagnetic and antiferromagnetic layers was not negligible, despite the NiO(001) being a spin-compensated surface.